Coating for concrete, wood, metal, tanks, and sewage treatment plants where a coating with good chemical resistance is essential.
Mixing Ratio: 2:1. mixing can be facilitated by using a Jiffy mixer and a 600 RPM drill. Mix for a minimum of three minutes or until uniform color is obtained. Pot life 55 minutes at 77° F. Cure time 7 days at 77° F. Do not thin as solvents will prevent proper cure. Bring to 75° F to facilitate mixing and prevent shock on cold surfaces. Do not apply on surfaces under 40° F.
Depending on surface, acid etch and rinse thoroughly, sandblast or shotblast.
Apply by roller, squeegee, or airless spray.
1 year minimum in unopened containers
Use barrier creams and disposable rubber gloves. Wash with soap and water. Do not wash hands with solvents. Epoxies contain chemical compounds that may cause allergic skin and respiratory reaction. Harmful if swallowed. Do not get in eyes or on skin. Use only with adequate ventilation. Wash thoroughly after handling
Wash before epoxy has set with acetone, MEK, Xylene, or toluene, these are all flammable materials. After scraping off excess material, use rags and solvent to finish cleanup. See above handling precautions.
| 15 Gallon kits | 3-Gallon kits | 1-Gallon kits/2 kits per case | |
| Gross Weight | 149 lbs. | 30 lbs. | 11 lbs. Per gallon |
| Cube | 3.3 cubic feet | 1 cubic foot | .5 cubic feet |
Proper Shipping Name: Adhesives, N.O.S.
Motor Freight Class: Adhesives, N.O.S.
Item 4620 (S-5)-Class 60
1. Sample: Chemi-cote, 2 component epoxy, lot #098519
2. Tests: Chemical solvent resistance
ASTM D1308 (covered) 24 hours
3. Test results
|
|
|
|
| 1. Oleic acid | mars and softens top film | decrease in reflectance (small blisters) |
| 2. Xylene | softens film and reduces gloss | slightly softens and mars (small blister) |
| 3. 30% Hcl | blisters and whitening | slightly decolorizes (lighter) |
| 4. 10% Hc103 | reacts and destroys surface gloss | slightly decolorizes (lighter) |
| 5 50% H2So4 | renders surface dull; blisters | slightly decolorizes (lighter) |
| 6. 43% Phoshoric Acid | mars and softens film, blisters | destroys gloss, decolorizes (blisters) |
| 7. 10% Chromic Acid | marked surface and yellows | stains - slightly yellowish |
| 8. Toluene | softens and destroys surface gloss | slight softening |
| 9. Acetone | softens and blisters | softens and a decrease in gloss (small blisters) |
| 10. MEK | softens; destroys surface properties | softens and mars surface |
| 11. Unleaded Gas | no effect | no effect |
| 12. Mecl2 | dissolves and detaches from substrate | softens |
| 13. 10% NaOH | surface O.K. at 6 hours | no effect |
| 14. Urine | no effect | no effect |
| 15. 10% Acetic Acid | erodes and forms blisters | erodes, softens and a decrease in gloss (slight blistering) |
| 16. Detergent | no effect | no effect |
| 17. Methanol | softens, gloss loss, slight blistering | softens; a decrease in gloss |
| 18. Wine | mars and detroys surface gloss | no effect |
| 19. Coca Cola | no effect | no effect |
| 20. Ethyl Acetate | mars and softens surface | mars and softens |
| 21. J.P. Alcohol | noeffect | no effect |
| 22. 5% Hydrogen Peroxide | reacts with surface, blisters | no effect |
| 23. Chloroform | dissolves | dissolves; softens surface (slight blistering) |